Processing Technique and PerformanceEvaluation of High-Modulus Organic/Inorganic Puncture-Resisting Composites

The development of low-cost organic/inorganic puncture-resisting composites is suggested to improve their puncture resistance and thermal insulation properties. In this paper, recycled high modulus Kevlar fiber and glass fabric were used together with polyester/lowmelting polyester nonwovens. The result shows that the static puncture resistance improves proportionally with Kevlar fibers; but the dynamic puncture resistance remains the same at first and then rises up to 20 wt % for Kevlar fibers. The increasing low-melting polyester fibers on the surface result in an upward and then downward trend for both static and dynamic puncture resistances. The additional polyester/low-melting polyester nonwovens are beneficial for the improvement of puncture resistances. Moreover the thermal conductivity of all the composites is in range of 0.015-0.025 W/m·K. According to the results, Kevlar fibers are also shown to be advisable reinforcement to achieve better tensile and bursting strengths.

Badano możliwości zwiększenia odporności na przebicie oraz odporności termicznej tanich organiczno-nieorganicznych kompozytów. W badaniach stosowano wysoko modułowe włókna Kevlar z recyklingu oraz tkaninę z włókien szklanych łącznie z włókninami wykonanymi z niskotopliwego poliestru. Stwierdzono, że statyczna wytrzymałość na przebicie zwiększa się proporcjonalnie z ilością włókien Kevlar, ale dynamiczna wytrzymałość na przebicie pozostaje początkowo taka sama, a następnie wzrasta do zawartości włókien Kevlar 20%. Zastosowanie niskotopliwych włókien poliestrowych powoduje tendencje wzrastające, a następnie malejące dla wytrzymałości statycznej i dynamicznej. Stwierdzono, że dodatek włókien Kevlar jest korzystny dla wytwarzanych kompozytów.