Examination of Selected Thermal Properties of Basalt Composites

A composite based on basalt fabric was produced because of its good thermal and mechanical properties. As a result of the reactive magnetron sputtering technique, a layer of aluminium and zirconium (IV) oxide 200 nm thick was deposited on Mylar film, which was adhered to the surface of the basalt fabric using a special adhesive glue and silicone. The variants of composites prepared were subjected to contact resistance tests at a contact temperature of 100 °C and 250 °C, as well as to resistance to thermal radiation tests. The tests carried out on the composites obtained showed an improvement of tested parameters.

W pracy wytworzono kompozyt na bazie tkaniny bazaltowej ze względu na jej dobre właściwości termiczne i mechaniczne. W wyniku zastosowania techniki reaktywnego rozpylania magnetronowego na folii Mylar osadzono warstwę aluminium i tlenku cyrkonu o grubości 200 nanometrów, którą przyklejono na powierzchnię tkaniny bazaltowej poprzez zastosowywanie kleju oraz silikonu. Przygotowane warianty kompozytów poddano badaniom odporności na ciepło kontaktowe dla temperatury kontaktu 100 °C i 250 °C oraz odporności na promieniowanie cieplne. Przeprowadzone na kompozytach badania wykazały poprawę badanych parametrów.