Preparation of Polypyrrole/Polyurethane Foam Composite Material

Firstly, the paper focused on the polyurethane foam soaking process with pyrrole solution, and discuss the estimated electro-mechanical properties of the modified PU foam. Secondly, scanning electron microscopy (SEM) micrographs were collected to understand the polypyrrole distribution inside the foam. The results show that the chemical polymerisation parameters needed to realise this amount of polypyrrole in the foam were 0.1 mol/L of pyrrole, a mole ratio of 1:2.25, an oxidation temperature of 12 ± 3 °C, and an oxidation time of 2 hours. SEM images of the samples prepared with the modified approach showed a continuous layer of about 10-15 μm thickness of the polypyrrole attached to the surface of the PU foam.

W artykule skoncentrowano się na procesie namaczania pianki poliuretanowej roztworem pirolu i omówiono oszacowane właściwości elektromechaniczne zmodyfikowanej pianki PU. Następnie zbadano rozkład polipirolu wewnątrz pianki przy zastosowaniu skaningowego mikroskopu elektronowego (SEM). Wyniki pokazały, że parametry polimeryzacji chemicznej potrzebne do uzyskania odpowiedniej ilości polipirolu w piance wynosiły 0,1 mol/l pirolu, stosunek molowy wynosił 1:2,25, temperatura utleniania wynosiła 12 ± 3 ° C i czas utleniania 2 godziny. Obrazy SEM próbek przygotowanych zgodnie ze zmodyfikowanym podejściem pokazały ciągłą warstwę o grubości około 10-15 μm polipirolu na powierzchni pianki PU.