The paper addresses the microsegregation of Mn, Mo, Cr, W, V, Si, Al, Cu and P in the white cast iron. Eutectic alloy with the content of 4.25% C was studied. The white cast iron was directionally solidified in the vacuum Bridgman-type furnace at a constant pulling rate v=83 μm/s and v=167 μm/s and at a constant temperature gradient G = 33.5 K/mm. The microstructural research was conducted using light and scanning electron microscopy. The microsegregation of elements in ledeburite was evaluated by EDS measurements. Content of elements in ledeburitic cementite and ledeburitic pearlite was determined. The tendency of elements to microsegregation was found dependent on the solidification rate. Microsegregation of elements between pearlite and cementite structural constituents has been specified. The effect of solidification rate on the type and intensity of microsegregation in directionally solidified eutectic white cast iron was observed. A different type of microsegregation was observed in the components of ledeburite in cementite and pearlite.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00