Ink based on poly(3,4-ethylene dioxythiophene), poly(sulfonostyrene) and silver nanoparticles (PEDOT/PSS/SNP) blends for fabrics printing

The influence of co-solvents such as: dimethylsulfoxide (DMSO), isopropyl alcohol (IPA), ethylene glycol (EG), ethanol (EtOH) and deionized water (DI) on the properties of ink based on poly(3,4--ethylene dioxythiophene), poly(sulfonostyrene) and silver nanoparticles (PEDOT/PSS/SNP) blends was investigated. The ink was obtained by the ultrasonic dispersion method by mixing PEDOT, PSS and SNP and then adding co-solvents. The ink was applied to the cotton fabric by printing method. The structure, electrical and functional properties of fabrics were investigated. The increase in electrical conductivity was found as a result of the phase separation between PEDOT and PSS due to the use of co-solvents. SEM micrographs showed good adhesion of the ink to the cotton fiber, which was confirmed by the FTIR method. The developed ink has great application potential, especially in electronic devices for biomedical purposes.

Zbadano wpływ współrozpuszczalników, takich jak: dimetylosulfotlenek (DMSO), alkohol izopropylowy (IPA), glikol etylenowy (EG), etanol (EtOH) i dejonizowana woda (DI) na właściwości atramentu otrzymanego na bazie mieszaniny poli(3,4-etyleno dioksytiofenu), poli(sulfonostyrenu) i nanocząstek srebra (PEDOT/PSS/SNP). Atrament otrzymano metodą dyspersji ultradźwiękowej poprzez wymieszanie PEDOT, PSS i SNP, a następnie dodanie współrozpuszczalników. Na tkaninę bawełnianą atrament nanoszono metodą druku. Zbadano strukturę, właściwości elektryczne i funkcjonalne tkaniny. Stwierdzono zwiększenie przewodnictwa elektrycznego jako efekt rozdziału faz między PEDOT i PSS na skutek zastosowania współrozpuszczalników. Mikrofotografie SEM wykazały dobrą adhezję atramentu do włókna bawełnianego, co potwierdzono metodą FTIR. Opracowany atrament ma duży potencjał aplikacyjny, zwłaszcza w urządzeniach elektronicznych do celów biomedycznych.