Mechanically, composite laminates perform exceptionally well in-plane but poorly out-of-plane. Interlaminar damage, known as "delamination," is a major issue for composite laminates. Results from Mode-I and Mode-II experimental testing on twill-woven carbon fiber reinforced (CFRP) laminates are analyzed in this paper. Composite Mode-I fracture toughness was determined using three different methods in accordance with ASTM D5528: modified beam theory, compliance calibration, and a codified compliance calibration. Two methods, the Compliance Calibration Method and the Compliance-Based Beam Method, were used to determine the Mode-II fracture toughness in accordance with ASTM D7905. Stick-slip behavior is quite evident in the composite's ModeI fracture toughness test findings. The MBT technique's Ic values for initiation and propagation are 0.533 and 0.679 KJ/m2 , respectively. When comparing the MBT approach to the industry-standard ASTM procedure for determining fracture toughness Mode-I, the MBT method was shown to be highly compatible. Furthermore, the IIc values for the CBBM technique are 1.65 KJ/m2 for non-pre cracked and 1.4 KJ/m2 for pre-cracked materials. The CBBM method shows a good method to evaluate fracture toughness Mode-II, due to not needing to monitor the length of the crack during delamination growth to get the value of the fracture toughness.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00