Wettability of the surface of bacterial cellulose film modified with the ion implantation

Wettability of the surface of bacterial cellulose film modified with low energy ion implantation The paper presents the preliminary results of the modification on the water wettability of cellulose, using ion implantation method. Two kinds ions of the noble gases, i.e. helium and argon were implanted with fluences of 1e15 nand 1e16 cm-2, and with the ion energy of 60 keV. The measurements of the contact angle values show the different influence of both types ions on the hydrophobicity of the modified cellulose, but the hydrophobicity of implanted cellulose increases in all cases. The real investigations were supplemented with the modelling results of the depth profiles of the implanted ions and the main parameters of the modelled peaks.

Zwilżalność powierzchni celulozy bakteryjnej modyfikowanej metodą implantacji jonów. Artykuł przedstawia wstępne wyniki modyfikacji na zwilżalność wodą implantowanej jonami celulozy. W badaniach wykorzystano dwa rodzaje gazów szlachetnych, tj. hel i argon. Implantowane dawki wynosiły 1e15 i 1e16 cm-2, a energia jonów 60 keV. Pomiary kąta zwilżania pokazują różny wpływ obydwu typów jonów na hydrofobowość modyfikowanej celulozy, jednakże hydrofobowość wzrasta we wszystkich przypadkach. Badania zostały uzupełnione wynikami modelowania głębokosciowych profili implantowanych jonów i głównych parametrów modelowanych pików.