The objective of this research is to investigate observable process changes during multi-layer friction surfacing of EN AW 6060 aluminum, whether for repair, remanufacturing, or new part manufacturing. In this study, friction surfacing was performed with a 10-mm-diameter rod of EN AW 6060 aluminum at spindle speeds ranging from 1000 to 7000 rpm to create up to three layers of 40-mm-long deposits on a substrate of the same alloy. The process forces and layer temperatures were observed. Post-process measurement of flash geometry, layer geometry and microhardness were conducted with the motivation to understand the impact of multi-layer depositions on performance and identifying acceptable conditions required to achieve acceptable build quality. The thickness, deposition and joining efficiency of layers in the multilayer configuration remained consistent. Friction surfacing of EN AW 6060 aluminum allowed for high deposition rates of 9 kg/hr, when compared to other metal additive technologies.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00