Effects of Yttrium (Y) Substitution by Cerium (Ce) on Microstructure and Corrosion Behavior of Near-Equiatomic Alniy Medium-Entropy Amorphous Alloy Ribbons

Tytuł:
Effects of Yttrium (Y) Substitution by Cerium (Ce) on Microstructure and Corrosion Behavior of Near-Equiatomic Alniy Medium-Entropy Amorphous Alloy Ribbons
Autorzy:
Zhang, Shuyan
Zhang, Zhibin
Wang, Xin
Gao, Yangyang
Liang, Xiubing
Powiązania:
https://bibliotekanauki.pl/articles/2106589.pdf
Data publikacji:
2022
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
medium-entropy amorphous alloys
corrosion behavior
thermal stability analysis
microstructure
cerium content
Źródło:
Archives of Metallurgy and Materials; 2022, 67, 2; 637--643
1733-3490
Język:
angielski
Prawa:
CC BY-NC-ND: Creative Commons Uznanie autorstwa - Użycie niekomercyjne - Bez utworów zależnych 3.0 PL
Dostawca treści:
Biblioteka Nauki
Artykuł
  Przejdź do źródła  Link otwiera się w nowym oknie
Through partially replacing Y element, Ce was added into near-equiatomic AlNiY medium-entropy amorphous alloy (denoted as MEAA) ribbons by the melt spinning process in this study. The differences of microstructure, thermal stability, hardness and corrosion resistance of Al33.3Ni33.3Y33.4-xCex(x = 0, 2, 5, 8, 13) alloy ribbons were investigated by X-ray diffraction (XRD), scanning electron microscope (SEM), differential scanning calorimeter (DSC) and Vickers-type hardness tester. The anti-corrosion performance in 3.5 wt.% NaCl solution of alloy ribbons was investigated elaborately through the general potentiodynamic polarization curves (Tafel) and electrochemical impedance spectroscopy (EIS). Results suggested that all ribbon samples could remain amorphous structure and the hardness are all above 510 HV0.1. With the increase of Ce content, the thermal stability begins to be gradually lower. However, according to the analysis of crystallization kinetics, all types of MEAA ribbons presents the relatively prominent thermal stability compared with traditional Al-based amorphous alloys. The corrosion current density raises firstly, then shows a decreasing trend, and has a slight increase at last. Therefore, appropriate content of Ce element can improve the corrosion protection performance of alloy ribbons and the 5 at.% Ce MEAA ribbons exhibited the excellent corrosion resistance in this study.

Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies