Effect of high shear rate on the mechanical properties of polyethylene, poly(ethylene terephthalate), polystyrene, and polypropylene waste blend

The effect of high shear rate on the mechanical properties of polyethylene (PE), poly(ethylene terephthalate) (PET), polystyrene (PS), and polypropylene (PP) waste blend was investigated. The process was carried out at a temperature of 120°C using a counter-rotating twin-screw extruder. A constant screw speed of 250 rpm and a constant weight ratio of the PE/PET/PS/PP components of 1:1:1:1 were used. The preliminary research showed that the high shear rate had no effect on the impact strength. However, the significant improvement in the flexural properties was observed as compared to those obtained at a lower screw speed of 80–120 rpm.

Zbadano wpływ szybkości ścinania na właściwości mechaniczne mieszaniny odpadów polietylenu (PE), poli(tereftalanu etylenu) (PET), polistyrenu (PS) i polipropylenu (PP). Proces prowadzono w temperaturze 120°C przy użyciu przeciwbieżnej wytłaczarki dwuślimakowej. Stosowano stałą szybkość obrotową ślimaka 250 min-1 i stały stosunek masowy składników PE/PET/PS/PP 1:1:1:1. Wstępne badania wykazały, że duża szybkość ścinania nie miała wpływu na udarność. Zaobserwowano jednak znaczną poprawę właściwości mechanicznych przy zginaniu w porównaniu z uzyskanymi przy mniejszej prędkości ślimaka 80–120 min-1.