Analysis of the polymeric abrasive paste regeneration for abrasive flow machining

The influence of conditions and the sifting process efficiency of the worn-out polymeric abrasive paste containing silica (SiO2) and polymer chips remaining after the surface treatment were investigated. The abrasive paste regeneration process consisted of sifting the used paste through sieves of a vibrating screen, on which abrasive grains and polymer chips were recovered. The diameter of the sieve holes determined the size of the recovered abrasive grains and polymer chips, on the size of which the efficiency of the process depended. The lowest efficiency of the sifting process was obtained using a sieve with the holes diameter equal to the diameter of the grain and the polymer chips of the given fraction. The highest efficiency of the sifting process was obtained for a sieve with a diameter of 0.032 mm. The regenerated polymeric abrasive paste can be reused in the process of abrasive flow machining.

Z badano w pływ w arunków i wydajność procesu przesiewania zużytej polimerowej pasty ściernej zawierającej krzemionkę (SiO2) i pozostałe po obróbce powierzchni wióry polimerowe. Proces regeneracji pasty ściernej polegał na przesianiu zużytej pasty przez sita przesiewacza wibracyjnego, na których odzyskiwano ziarna ścierne i wióry polimerowe. Średnica otworów sita determinowała wielkość odzyskanych ziaren ściernych i wiórów polimerowych, od których wielkości zależała wydajność procesu. Najmniejszą wydajność procesu przesiewania uzyskano stosując sito o średnicy otworów równej średnicy ziarna oraz wiórów polimerowych danej frakcji, a największą sito o średnicy 0,032 mm. Zregenerowaną polimerową pastę ścierną można ponownie wykorzystać w procesie obróbki przetłoczono–ściernej.