This study focused on the fatigue and corrosion fatigue of maraging steel 18Ni (250). The 18Ni (250) samples were tested for axial fatigue in air and 3.5% NaCl solution. The effects of loading frequency and stress ratio on the fatigue strength of 18Ni (250) were studied. In air, the loading frequency was 10 Hz, and the stress ratio was 0.5. However, three loading methods were used in the 3.5% NaCl solution: (i) the loading frequency of 1 Hz and stress ratio of 0.5; (ii) the loading frequency of 1 Hz and stress ratio 0.1, and (iii) the loading frequency 5 Hz and stress ratio 0.5. The corrosion fatigue strength of samples in the 3.5% NaCl solution was 63.3% lower than that of the samples in air. The fractures in the samples were observed after the test.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00