Ceramic-metal composites are usually prepared by sintering ceramic with metal or metal oxide powders. An alternative technique is sintering ceramic powders coated by metal film. In the present study, the Ni coated Al$\text{}_{2}$O$\text{}_{3}$ powder was obtained by chemical reduction reaction. We used the phosphate bath for deposition of nickel-phosphorus on the surface of Al$\text{}_{2}$O$\text{}_{3}$ powder. The thickness and chemistry of Ni-P coating depend on the time and the parameters of the reaction process. Particles of Ni-P precipitate from a solution in two different forms: (a) spherical nanoparticles of Ni-P (50 nm) which grow on the surface of Al$\text{}_{2}$O$\text{}_{3}$ powder and can form tight, one diameter thick film; (b) large agglomerates of loosely connected spherical nanoparticles with a 50÷150 nm diameter. The method proposed in this study allows obtaining Al$\text{}_{2}$O$\text{}_{3}$ powder covered with Ni-P nanoparticles in the forms of thin film or single nanoparticles, mixed with loose Ni-P agglomerates.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00