The aim of the work was to determine the diagrams of phase evolution under equilibrium conditions and numerical simulation of austenite phase transformations under non-equilibrium conditions, as well as to determine CCT (Continuous Cooling Transformation) and TTT (Temperature Time Transformation) diagrams with the use of JMatPro software. The subject of the analysis were two newly elaborated multiphase steels assigned for production of forgings: steel A, containing of 0.165% C, 2% Mn, 1.11% Si and steel B, containing 0.175% C, 1,87% Mn, 1% Si, 0.22% Mo and Ti and V microadditions at a concentration of 0.031% and 0.022%, respectively. The performed simulation revealed that the investigated steels have similar critical temperatures under equilibrium conditions: Ac1 ~ 680°C, Ac3 ~ 830°C. The chemical composition of steel B and the interaction of Mo, Ti and V in particular, determine that diffusion transformations, i.e. ferritic and pearlitic, in the elaborated CCT and TTT diagrams are significantly shifted to longer times in relation to the position of these transformations in the diagrams for steel A. A distinct delay also concerns the bainitic transformation. Moreover, it was found that the MS temperature of steel B is slightly lower. The determined CCT and TTT diagrams are essentially helpful in the development of heat and thermo-mechanical treatment conditions for new steel grades.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00