The paper presents the experimental results of fabrication and characterization of ceramic- elastomer composites. They were obtained using pressure infiltration of porous ceramics by elastomer As a result the composites in which two phases are interpenetrating three-dimensionally and topologically throughout the microstructure were obtained. In order to enhance mechanical properties of preforms a high isostatic pressure method was utilized. The obtained ceramic preforms with porosity gradient within the range of 20-40% as well as composites were characterized by X-ray tomography. The effect of volume fraction of pores on residual porosity of composites was examined. These results are in accordance with SEM images which show the microstructure of composites without any delaminations and voids. Such composites exhibit a high initial strength with the ability to sustain large deformations due to combining the ceramic stiffness and rubbery elasticity of elastomer. Static compression tests for the obtained composites were carried out and the energy dissipated during compression was calculated as the area under the stress-strain curve. The dynamic behavior of the composite was investigated using the split Hopkinson pressure bar technique. It was found that ceramic-elastomer composites effectively dissipate the energy. Moreover, a ballistic test was carried out using armor piercing bullets.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE W OKRESIE WAKACYJNYM BIBLIOTEKA BĘDZIE FUNKCJONOWAŁA W ZMIENIONYCH GODZINACH::
od 15 do 31 lipca:
Wypożyczalnia i Czytelnia Główna:
9.00 - 15.00
(poniedziałek-piątek)
Czytelnia Działu Zbiorów Specjalnych:
9.00 - 15.00
(poniedziałek-piątek)
od 1 do 31 sierpnia:
BIBLIOTEKA BĘDZIE NIECZYNNA
UWAGA:
Zwrotu wypożyczonych materiałów można dokonać u dyżurującego bibliotekarza w Wypożyczalni Głównej od 9.00 do 15.00.
Na pozycje, których termin zwrotu przypadnie od 1 do 31 sierpnia, wprowadzona zostanie prolongata (nowy termin zwrotu – 6 września).