It is shown that ammonothermal method can be successfully used to synthesize GaN powder of good crystallographic quality from ammonia solution at high pressure and a moderate temperature. The size of obtained GaN powder grains was of a few micrometers. The improvement of the powder crystalline quality (examined by X-ray rocking curve, scanning electron microscopy and luminescence measurements) with increasing molar proportion of mineralizer was observed. It was therefore possible to conclude that high molar proportion of mineralizer in ammonia solution plays a crucial role in the polycrystal growth process. Visible luminescence of high efficiency from the GaN powder was found.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00