Analysis of the Temperature Value in Contact Steel – Soil Material in Relation to the Type of Construction Material

The article presents a study of the friction temperature at the contact soil soil-material. For the tests, samples of 38GSA steel padded with El-Hard 63 electrode and Hardox 600 steel were selected. The experiment was carried out in laboratory conditions using the “rotating bowl” method in two soil types with different humidity. For light soil abrasive, the change in humidity increased the mass consumption in the wet soil almost twice for Hardox 600 steel and 1.5 times for the steel 38GSA welded. However, in the middle soil, the 38GSA steel was characterized by a higher wear value. The research shows that there were significant differences in consumption between the tested materials.

W artykule przedstawiono badanie temperatury tarcia w styku masa glebowa-materiał. Do badań wytypowano próbki ze stali 38GSA napawanej elektrodą El-Hard 63 oraz stal Hardox 600. Eksperyment przeprowadzono w warunkach laboratoryjnych metodą „wirującej misy” w dwóch rodzajach gleb o różnej wilgotności. Dla lekkiej glebowej masy ściernej zmiana wilgotności wzrost zużycia masowego spowodowała wzrost zużycia masowego w glebie mokrej prawie dwukrotnie dla stali Hardox 600 i półtorakrotnie dla stali 38GSA napawanej. Natomiast w glebie średniej wyższą wartością zużycia charakteryzowała się stal 38GSA napawana. Z przeprowadzonych badań wynika, iż pomiędzy badanymi materiałami odnotowano istotne różnice w zużyciu.