Wear resistance characteristics of thermo-chemically treated structural steels

The article presents results of investigations of wear resistance by friction, employing the “3 cylinder – cone” method, of selected structural steels subjected to given thermo-chemical treatment, i.e. nitriding, carburizing, and precipitation hardening after nitriding. The investigated steels were C45, 21NiCrMo2, 18HGT, and 41Cr4. These materials, after thermo-chemical treatment undergo metallurgical characteristics of diffusion layers formed on steel. It was observed that proportionality exists between their wear resistance and the value of surface unit loading. Moreover, the friction – wear properties of these layers exhibited certain differences, depending on their microstructure and chemistry.

Artykuł ten przedstawia wyniki badań odporności na zużycie, wykorzystując metodę „3 wałeczki – stożek”, dotyczące wybranych stali konstrukcyjnych poddanych określonej obróbce cieplno-chemicznej, tj. azotowaniu, nawęglaniu i utwardzaniu wydzieleniowemu po azotowaniu. Badanymi stalami były: C45, 21NiCrMo2, 18HGT i 41Cr4. Stale te po obróbce cieplno-chemicznej podlegają ocenie metaloznawczej warstw dyfuzyjnych wytwarzanych na stali. Zauważa się ich proporcjonalną zależność pomiędzy odpornością na zużycie a wartością nacisku jednostkowego powierzchni. Jednakże własności tarciowo-zużyciowe wyraźnie różnią się, zależąc od ich mikrostruktury i budowy chemicznej.