The Effect of Surface Texture of Steel Disc on Friction and Fretting Wear Wpływ struktury geometrycznej powierzchni tarcz stalowych na tarcie i zużycie frettingowe
Fretting tests were performed using an Optimol SRV5 tribotester in a ball-on-flat scheme. Balls from 100Cr6 steel of 60 HRC hardness and diameters of 10 mm co-acted with discs from 42CrMo4 steel of 47 HRC hardness under dry gross fretting conditions. Tests were performed at 30°C and 25–35% relative humidity, and the number of cycles was 18000. During each test, the normal load was kept constant. Six sets of experiments were conducted. Discs had different surface textures as the result of machining. It was found that the lowest coefficients of friction were obtained for anisotropic surfaces when ball movements were perpendicular to main disc texture directions.
W badaniach zastosowano tester tribologiczny Optimol SRV5. Kulka ze stali 100Cr6 o twardości 60 HRC kontaktowała się z tarczą o średnicy 10 mm wykonaną ze stali 42CrMo4 o twardości 47 HRC w warunkach frettingu. Temperatura wynosiła 30°C, wilgotność względna 25–35% przy liczbie cykli równej 18000. Tarcze charakteryzowały się zróżnicowaną strukturą geometryczną powierzchni uzyskaną w wyniku obróbki. Najmniejsze współczynniki tarcia osiągnięto, kiedy ruch kulki odbywał się prostopadle do głównego kierunku ukształtowania powierzchni tarczy.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00