Microstructure and Resistance to Abrasive and Corrosive Wear of a Chromosiliconized Layer on C45 Steel Substrate

The paper presents the results of investigation of the microstructure and resistance to the abrasive and corrosive wear of a chromosiliconized layer on C45 steel substrate. The chromosiliconizing process was carried out at 1000°C for 6 hours by the powder pack method. Microstructure, chemical and phase composition of the layer as well as surface roughness, thickness, and hardness measurements were carried out. Tribocorrosion tests were conducted with the use of a wear tester composed of three rollers and a cone. The frictional resistance of a chromosiliconized layer was investigated under exposure to a corrosive medium of an aqueous suspension of quartz sand. Chromosiliconizing of C45 steel influenced the resistance to wear of the layers during friction processes in the abrasive and corrosive environment.

Omówiono wyniki badań dotyczące mikrostruktury warstwy chromokrzemowanej wytworzonej na podłożu stali C45 w kształtowaniu odporności na zużycie podczas tarcia ścierno-korozyjnego. Proces chromokrzemowania realizowano przy temperaturze 1000°C przez 6 godzin metodą proszkową. Przeprowadzono badania mikrostruktury, składu chemicznego i fazowego warstwy, a także pomiary chropowatości jej powierzchni oraz grubości i twardości. Badania zużycia podczas tarcia warstwy chromokrzemowanej narażonej na oddziaływanie zawiesiny wodnej piasku kwarcowego przeprowadzono za pomocą tribometru typu trzy wałeczki/ stożek. Chromokrzemowanie stali C45 zwiększyło jej odporność na zużycie w procesie tarcia w warunkach oddziaływania korozyjnego.