The Impact of the Selected Parameters of FDM Manufacturing Technology on Tribological Performance of ABS–Steel Pair under Dry Friction

The paper presents the result of tribological test of ABS and steel samples sliding under dry friction. Polymeric samples were manufactured of ABS material using FDM technology. Testing was carried out in unidirectional sliding in a ring-on-flat contact in a PT-3 tribometer. The scope of tested parameters included volumetric and mass wear, the friction coefficient, and polymeric specimen temperature. Polymeric specimens used in the study were manufactured at various settings of the 3D printing process such as the orientation of the specimen in print with respect to the printer building tray and the thickness of a single layer of the deposited material. Comparisons of the impact of these parameters on tribological performance of the sliding contact were analysed.

Przedstawiono wyniki badań tribologicznych pary ABS – stal w warunkach tarcia suchego. Polimerowa próbka została wykonana z materiału ABS przy użyciu metody FDM. Testy jednokierunkowego tarcia w układzie pierścień – tarcza przeprowadzono na Tribometrze PT-3. Analizowanymi parametrami były zużycie masowe i objętościowe, współczynnik tarcia oraz temperatura próbki polimerowej. Próbki polimerowe zostały wyprodukowane przy różnych parametrach procesu druku 3D, takich jak: orientacja próbki w stosunku do platformy drukarki oraz grubość drukowanej warstwy. Przeprowadzono szczegółową analizę wpływu tych parametrów na charakterystyki tribologiczne badanego skojarzenia ślizgowego.