Investigation of wear resistance of selected materials after slide burnishing process

The article presents the research on the impact of slide burnishing process carried out with use of various ceramics on friction and wear of steel elements. In addition, surfaces after grinding, lapping and polishing processes were tested. The tribological couple was made of steel discs, toughened to a hardness of 40 ± 2 HRC, and balls made of 100Cr6 steel with a hardness of 62 HRC. The tests were carried out at three sliding speeds: 0.16 m/s, 0.32 m / s and 0.48 m/s. The research proved the possibility of improving selected tribological properties of friction pairs thanks to the use of slide burnishing process and also allowed to establish a number of relationships between the parameters characterizing the surface topography and the tribological parameters.

W artykule przedstawiono wyniki badań wpływu procesu nagniatania ślizgowego realizowanego z wykorzystaniem różnych ceramik na wielkość zużycia oraz siłę tarcia elementów stalowych. Dodatkowo badaniom poddano powierzchnie po procesach szlifowania, docierania oraz polerowania. Skojarzenie materiałowe stanowiły tarcze stalowe ulepszone cieplnie do twardości 40±2 HRC oraz kulki ze stali100Cr6 o twardości 62 HRC. Badania zrealizowano przy trzech prędkościach poślizgu: 0,16 m/s, 0,32 m/s oraz 0,48 m/s. Badania udowodniły możliwość poprawy wybranych właściwości tribologicznych par trących dzięki zastosowaniu procesu nagniatania ślizgowego a także pozwoliły na ustalenie szeregu zależności pomiędzy parametrami charakteryzującymi strukturę geometryczną powierzchni oraz parametrami tribologicznymi.