Persistence of the thin layers of transition metal carbides in contact with liquid NiBSi alloy

The article presents the results of study on interaction between the liquid NiBSi alloy and solid, thin, micrometer-range layers of transition metal carbides of IVB - VIB groups of the periodic table. The reactive magnetron sputtering method was adopted to deposit of these layers on molybdenum substrates. Carbide layers are destroyed in contact with liquid alloy by dissolving, intensified by the penetration of the liquid along the coating ‒ substrate interface. The strong interaction between liquid NiBSi and both the carbide ceramics and the refractory metal substrate was revealed. The effect intensity differs somewhat for both tested carbide groups: VIB (relatively fast) and IVB (less intense).

W artykule przedstawiono wyniki badań oddziaływania ciekłego stopu NiBSi z litymi, cienkimi, mikrometrowymi warstwami węglików metali przejściowych IVB – VIB grup układu okresowego pierwiastków. Do nanoszenia tych warstw na podłożach molibdenowych adoptowano metodę reaktywnego rozpylania magnetronowego. Warstwy węglików ulegają destrukcji w trakcie kontaktu z ciekłym stopem poprzez ich rozpuszczanie, intensyfikowane penetracją cieczy po granicy powłoka - podłoże. Świadczy to o silnym oddziaływaniu cieczy NiBSi zarówno z ceramiką węglikową, jak i podłożem z metalu trudnotopliwego. Efekt ten jest zróżnicowany dla węglików metali grup VIB (stosunkowo szybki) i IVB (mniej intensywny).