Defect studies of Nb irradiated with 10 MeV electrons were performed in the present work by means of positron annihilation spectroscopy. The lattice defects were characterized by positron lifetime spectroscopy. Moreover, defect depth profiles were studied by slow positron implantation spectroscopy. The experimental investigations were accompanied by first principles theoretical calculations of positron parameters. It was found that irradiation-induced vacancies in Nb specimens are surrounded by H, which causes a shortening of the lifetime of trapped positrons. The influence of a Pd and Cr over-layer on the H concentration in the Nb specimens was examined.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00