Microstructure by the Mössbauer spectroscopy and approach to magnetic saturation in the bulk amorphous $Fe_{61}Co_{10}Me_7Y_2B_{20}$ ($Me_7$=$Y_7$, $Y_6Ti_1$ or $Zr_{2.5}Hf_{2.5}W_2$) alloys are investigated. The bulk amorphous $Fe_{61}Co_{10}Zr_{2.5}Hf_{2.5}W_2Y_2B_{20}$ alloy exhibits the best thermal stability and remains amorphous up to 901 K. Moreover, the quasi-dislocations dipoles present in this amorphous alloy have the largest width equal to 6.7 nm. After annealing this alloy below the crystallization temperature the enhancement of both the average hyperfine field and its standard deviation is observed which points to the increase in the atom packing density due to the decay of quasi-dislocation dipoles. After the annealing at 901 K the small amount of the crystalline α-FeCo phase is presented in this alloy. The same crystalline phase appears in the bulk $Fe_{61}Co_{10}Y_8Ti_1B_{20}$ and $Fe_{61}Co_{10}Y_9B_{20}$ alloys after annealing at 750 K and 840 K, respectively.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00