The article presents an application of X-ray microtomography for identification of the carbonation zone in concrete material.
A concrete specimen subjected earlier to harsh environmental conditions is investigated. The material is firstly checked with the
use of chemical corrosion indicators and then is subjected to microstructural analysis performed with the use of X-ray microtomography.
Two different settings of scanning parameters are applied implying the image resolutions of approximately 14 μm per
1 pixel and about 7 μm per 1 pixel, respectively. The results obtained are then compared and analyzed. The depth of the carbonation
zone is evaluated based on the attenuation curve. The paper highlights also the significance of the corrosion phenomenon in concrete
structures. Details of the deterioration mechanisms in concrete are shortly presented.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00