Polycrystalline diamond tools wear during machining of cemented carbides produced by laser cladding

This paper presents the analysis of tool’s flank wear, and surface roughness generated during turning of chromium-carbides based on chrome-nickel alloy. The influence of cutting speed and feed per revolution on the investigated quantities was presented. The TPGN110304F cutting inserts made of polycrystalline diamond (KD100) were applied in the research. Tool’s flank wear VB_c was measured on the microscope. The surface profiler Hommel Tester T500 was applied to the measurements of surface roughness (Ra parameter). The machinability valuation of sintered carbide was the primary objective of the research. It was proved, that the chromium-carbides are difficult to cut materials, therefore, the application of polycrystalline diamond (PCD) tool is justified.

W pracy przedstawiono analizę wyników badań procesu toczenia wałka z węglika chromu o osnowie niklowo-chromowej. Określono wpływ posuwu oraz prędkości skrawania na zużycia ostrza i chropowatość powierzchni. Stosowano płytki wymienne TPGN110304F z narożem z polikrystalicznego diamentu (KD100). Pomiar szerokości powierzchni starcia na powierzchni przyłożenia VB_c prowadzono za pomocą mikroskopu świetlnego. Do pomiaru chropowatości powierzchni – parametru Ra użyto profilografometru Hommel Tester T500 z oprogramowaniem TURBO DATAWIN. Celem prowadzonych badań procesu toczenia wałka z warstwą wierzchnią z węglików spiekanych napawanych laserowo było ustalenie ich skrawalności, w zależności od przyjętego kryterium. Stwierdzono, że węglik chromu jest materiałem trudno skrawalnym. Zastosowanie ostrzy z polikrystalicznego diamentu jest uzasadnione.