Depth distribution of implanted species and microstructure of oxygen-containing Czochralski grown silicon (Cz-Si) implanted with light ions (such as $H^{+}$) are strongly influenced by hydrostatic pressure applied during the post-implantation treatment. Composition and structure of Si:H prepared by implantation of Cz-Si with $H_{2}^{+}$; fluence D = 1.7 × $10^{17} cm^{-2}$, energy E = 50 keV (projected range of $H_{2}^{+}$, $R_{p}(H)$ = 275 nm), processed at up to 923 K under Ar pressure up to 1.2 GPa for up to 10 h, were investigated by elastic recoil detection Rutherford backscattering methods and the depths distributions of implanted hydrogen and also carbon, oxygen and silicon in the near surface were determined for all samples. The defect structure of Si:H was also investigated by synchrotron diffraction topography at HASYLAB (Germany). High sensitivity to strain associated with small inclusions and dislocation loops was provided by monochromatic (λ = 0.1115 nm) beam topography. High resolution X-ray diffraction was also used.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00