Transport, magnetic and thermal properties of substitutional solid solution $Eu_{1 - x}Ca_{x}B_6$ single crystals (0 ≤ x ≤ 0.244) have been studied at 1.8 ≤ T ≤ 300 K and in magnetic fields up to 8 T. Calcium doping is shown to result in a metal-insulator transition, which occurs at x_{MIT} ≈ 0.2. In vicinity of metal-insulator transition the effect of colossal magnetoresistance is found to be very sensitive to Ca content, the amplitude varying from Δ = [ ρ (0)- ρ (8T)]/ρ(8T) ≈1.4 × $10^2$ to Δ ≈ 7.5 × $10^3$ for 0.14 ≤ x ≤ 0.16. The analysis of magnetic contribution to heat capacity shows that a large amount of magnetic entropy ( ≈ 30%) releases in $Eu_{0.845}Ca_{0.155}B_6$ when moving from the Curie temperature $T_{C}$ ≈ 5.5 K to the characteristic one T* ≈ 30 K. This observation as well as the large amplitude of low field colossal magnetoresistance effect and the deviation of magnetic susceptibility from the Curie-Weiss law detected for x = 0.155 compound in the interval $T_{C}$ ≤ T ≤ T* seem to be associated with magnetic phase separation induced by Ca doping.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00