The present paper focused on the analysis of the fracture surfaces of a new development insulated iron powder compound with the addition of the aluminium alloy in order to improve the mechanical properties. Results show that in the pressed state, mainly pores act as crack initiators and due to their presence the distribution of stress is inhomogeneous across the cross-section and leads to the reduction of the effective load bearing area. Investigation of fracture surfaces concluded that improvements in bonding during the pressing process and heat treatment can be helpful in the development of soft magnetic materials to give a suitable combination between pressing pressure, annealing temperature and time as well as magnetic properties.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00