The Features of Real Part of Admittance in the Nanocomposites $(Fe_{45}Co_{45}Zr_{10})_{x}(Al_2O_3)_{100 - x}$ Manufactured by the Ion-Beam Sputtering Technique with Ar Ions
The Features of Real Part of Admittance in the Nanocomposites $(Fe_{45}Co_{45}Zr_{10})_{x}(Al_2O_3)_{100 - x}$ Manufactured by the Ion-Beam Sputtering Technique with Ar Ions
The temperature and frequency dependences of the admittance real part σ (T, f) in granular $(Fe_{45}Co_{45}Zr_{10})_{x}(Al_2O_3)_{100 - x}$ nanocomposite films around the percolation threshold $x_{C}$ were investigated. The behaviour of σ (T, f) vs. the temperature and frequency over the ranges 77-300 K and 50 Hz-1 MHz, respectively, displays the predominance of an activation (hopping) conductance mechanism for the samples below the percolation threshold $x_{C}$ and of a metallic one beyond the $x_{C}$ determined as 54 ± 2 at.%. The mean hopping range d for the nanoparticles diameter D was estimated at different metallic phase content x.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00