In this work hyperfine fields of two-phase nanocrystalline Fe72Cu1.5Nb4Si13.5B9 alloys were studied in order to verify the existence of surface effects. To obtain a series of nanocrystalline samples with small grains of different sizes, a special non- -isothermal annealing procedure of an initially amorphous ribbon was applied. In the case of samples with a significant amount of crystallites, a high field (about 27.5 T) component of continuous part of the hyperfine field distribution was found that could be attributed to boundary regions between the grains and rest of the sample. The existence of the surface effects was confirmed in the magnetostrictive experiment.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00