The paper presents results of microstructure and magnetic properties studies of Nd8.5Tb1.5Fe83Zr1B6
ribbons obtained by melt-spinning technique. The samples were produced using the rapid cooling of liquid alloy
on the copper wheel, by applying three different linear velocities 20, 30, and 35 m/s. The microstructure of
obtained ribbons was examined using X-ray diffractometry and Mössbauer spectroscopy. Magnetic measurements
were performed using LakeShore vibrating sample magnetometer. The microstructure measurements were used
for quantitative and qualitative analysis of phase composition. Basing on results of structure studies combined
with magnetic measurements, the infl uence of phase composition on hysteresis loop behavior was described.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00