Multiferroic 0.5BiFeO3-0.5Pb(Fe0.5Ta0.5)O3 solid solution is a material that exhibits ferroelectric and
antiferromagnetic orderings in ambient temperature. The solid solution was obtained as a result of a conventional
reaction in a solid state. The obtained material is a dense, fine-grained sinter whose surface was observed by
scanning electron microscopy (SEM) and stoichiometry was confirmed by energy dispersive X-ray spectroscopic
(EDS) analysis. According to the X-ray powder diffraction (XRD) measurements, the main phase is R3c space
group with admixture of Pm-3m regular phase. Small contribution of pyrochlore-like phase was also observed.
Mössbauer spectroscopy suggested random distribution of Fe3+/Ta5+ cations in the B sites of ABO3 compound.
Reduction of the magnetic hyperfine field with an increase in the substitution of Ta5+ in Fe3+ neighbourhood
was also observed.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00