Positron annihilation spectroscopy (PAS) has been used to study the annealing behavior of cold rolled
Fe – 21 wt% Mn steel with 0.05 wt% C. After the initial annealing of defects shown by Doppler broadening
of the annihilation line, a slight increase in the annihilation line shape parameter, i.e., the so-called S parameter
and then its decrease in the temperature range between 225◦C and 450◦C indicates generation of new defects
and their subsequent annealing. This temperature range coincides with X-ray diffraction measurements, which
indicate reversion of deformation-induced ε-martensite. However, for annealing in this temperature range with
slow cooling of the sample, the formation of ferrite already starts. The results are compared with our previous
results for deformed austenitic stainless steel 1.4301 (EN) where only reversion of deformation-induced
α'-martensite was detected.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00