Influence of Co Doping on Crystal and Magnetic Properties of $Gd_2Cu_2In$

Physical properties of $Gd_2Cu_{2 - x}Co_{x}In$ (x = 0.1, 0.2, 0.3) samples are investigated. The paper brings results of X-ray diffraction, magnetometric as well as specific heat studies. It was found that only sample with x = 0.1 exhibits desired crystal structure. Other compositions show existence of impurities due to lack of dissolution Co atoms. For $Gd_2Cu_{1.9}Co_{0.1}In$ sample the Curie temperature of 92.5 K was evidenced. Thus, an enhancement of ferromagnetic correlations with comparison to $Gd_2Cu_2In$ sample was evidenced. It was found that $Gd_2Cu_{1.9}Co_{0.1}In$ sample exhibits magnetocaloric effect within broad temperature range.