Impact of Activator Content on the Process of Photodegradation of PP Non-Wovens

The paper presents the test results of non-wovens modified by an activator in different concentrations, produced by the spun bonding method. The aim of the research was to assess the photodegradation process of modified PP non-wovens in dependence on the selected concentration of the modifying agent in the fibre mass and the possibility of introducing a new range of PP non-wovens in agriculture. Non-wovens having a mass per unit area of 100 g/m2 were exposed to sunlight during its highest intensity for a period of four months, and UV irradiance was tested in a xenon lamp with radiation doses corresponding to exposure to sunlight. The samples were exposed to the same energy value of visible and UV radiation in a given series of exposure. For the variants of non-wovens tested, the tensile strength and mass per unit area were tested and the surface topography of the non-wovens analysed. Microscopic analysis of fibre damage in the modified non-wovens was carried out after different degrees of exposure to light. It was observed that PP non-woven samples exposed outdoors degraded more intensively than those tested in the Xenotest.

Praca przedstawia wyniki badań włóknin, modyfikowanych aktywatorem o różnym stężeniu, wytworzonych metodą spun bonded. Włókniny o masie powierzchniowej 100 g/m2 poddano ekspozycji na światło słoneczne w okresie największego natężenia słońca przez okres czterech miesięcy. Równolegle prowadzono badania natężenia promieniowania UV w lampie xenonowej. Próbki otrzymały jednakową wartość energii promieniowania widzialnego i UV w danej serii naświetlania. Dla badanych wariantów włóknin wykonano badania wytrzymałości na rozciąganie, masy powierzchniowej oraz dokonano analizy topografii powierzchni włóknin. Przeprowadzono analizę mikroskopową uszkodzeń włókien modyfikowanej włókniny po różnym stopniu naświetlenia.