Laminated Aluminum Composite Structure (LACS) has shown great potential for replacing traditional bulk aluminum parts, due to its ability to maintain low manufacturing costs and create complex geometries. In this study, a LACS, that consists of 20 aluminum layers joined by a structural tape adhesive, was fabricated and tested to understand its impact performance. Three impact tests were conducted: axial drop, normal and transverse three-point bending drop tests. Numerical simulations were performed to predict the peak loads and failure modes during impacts. Material models with failure properties were used to simulate the cohesive failure, interfacial failure, and aluminum fracture. Various failure modes were observed experimentally
(large plastic deformation, axial buckling, local wrinkling, aluminum fracture and delamination) and captured by simulations. Cross-section size of the axial drop model was varied to understand the LACS buckling direction and force response. For threepoint bending drop simulations, the mechanism causing the maximum plastic strain at various locations in the aluminum and adhesive layers was discussed. This study presents an insight to understand the axial and flexural responses under dynamic loading, and the failure modes in LACS. The developed simulation methodology can be used to predict the performance of LACS with more complex geometries.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00