The citrate gel method, similar to the polymerized complex method, was used to synthesize homogeneous tetragonal zirconia at 1000°C. Nanocrystalline tetragonal phase has been fully stabilized at wide temperature range with 10 mol.% CaO, MgO, and $Y_2O_3$ addition. Scanning electron microscopy, X-ray diffraction, and microhardness tests are used to characterize synthesized materials. The grain size and dislocation density were calculated from X-ray diffraction data. The examined material exhibits indentation size effect behavior. Results revealed that the Vickers and Knoop microhardness are dependent on indentation test load. Geometrically necessary dislocation model and modified proportional resistance model are used to analyze the load dependence of the microhardness. The highest hardness values were obtained for the samples with CaO addition; however the lowest values were acquired for sample stabilized with $Y_2O_3$ by using both Knoop and Vickers techniques. This situation might be explained using the Hall-Petch relation.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00