Magnetic properties of polycrystalline multiferroic $Bi_{0.65}La_{0.35}Fe_{0.5}Sc_{0.5}O_3$ synthesized under high-pressure (6 GPa) and high-temperature (1500 K) conditions were studied using a SQUID magnetometer technique. The temperature dependent static magnetic moment M was measured in both zero-field-cooled and field-cooled modes over the temperature range of 5-300 K in low magnetic field H=0.02 kOe. The field dependent magnetization M(H) was measured in magnetic fields up to 50 kOe at different temperatures up to 230 K after zero-field cooling procedure. A long-range magnetic ordering of the antiferromagnetic type with a weak ferromagnetic contribution takes place below $T_{N} ≈ 220 K$. Magnetic hysteresis loops taken below $T_{N}$ show a huge coercive field up to $H_{c}$ ≈10 kOe, while the magnetic moment does not saturate up to 50 kOe. A strong effect of magnetic field on the magnetic properties of the compound has been found. Below $T_{N}$ ≈220 K the derivatives of the initial magnetization curves demonstrate the existence of a temperature-dependent anomaly in fields of H=15÷25 kOe. The nature of the anomaly is unknown and requires additional study.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00