This paper presents the results of studies on the magnetic properties of the $Fe_{60}Co_{10}Mo_{2}Y_{8}B_{20}$ alloy. The samples were fabricated in the form of plates by the injection-casting method. The structure of the investigated alloy, in the as-quenched state and after annealing, was verified by using X-ray diffractometry. The magnetization curves as a function of temperature were measured by a force magnetometer. From thermomagnetic curves the Curie temperature of the alloy was determined. As a critical parameter β was chosen to be equal to 0.36 for these calculations, it confirmed that the alloys may be considered as ferromagnetic of the Heisenberg type. Additionally, using a vibrating sample magnetometer the magnetization and coercivity field were studied (in magnetic field up to 2 T).
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00