In the present investigation, we have studied leaching on polygrain Al-based quasicrystalline $(i-Al_{63}Cu_{25}Fe_{12})$ as well as crystalline (B2 phase; $Al_{55}Cu_{30}Fe_{15})$ alloy surfaces using a 10 mole NaOH solution. The surface was leached at varying times from 30 min to 8 h and subsequently characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy and energy dispersive X-ray analysis. Leaching of the samples for 30 min generated a homogeneous layer. However further leaching for 1-8 h yielded nano-size particles on the surface. Spherical microstructure has been observed on the Al-Cu-Fe crystalline surface whereas on the quasicrystalline surface a petal-like microstructure appeared. The implications of the evolution of different microstructures in the context of structure, stability and activity are discussed. The results are compared with the microstructure of leached polygrained samples containing a mixture of different surface orientations.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00