The coatings investigated in this paper were deposited via the magnetron sputtering of $AlN-TiB_2-Ti-Si_2$ target in Ar atmosphere. The investigation of structural-phase composition, element composition, morphology and mechanical properties before and after annealing up to 1350°C was carried out. The concentration of elements in the coating was changed after annealing at 900°C and further annealing at 1350°C (especially after annealing at 1350°C). The hardness of as-deposited coatings was 15 GPa, but after annealing at 1350°C the value of hardness increased up to 22÷23.5 GPa. The value of the viscoplastic index was 0.07. All this provide high damping properties of the coating, and amorphous-like structure makes promising the use of these coatings as diffusion barriers in the form of independent elements, and as a contacting layer in multilayer wear resistant coatings.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00