Wpływ procesu redukcji na właściwości strukturalne i mechaniczne szkieł tlenkowych z grupy (Pb,Bi)-(Si,Ge)-O Influence of reduction process on the structural and mechanical properties of (Pb,Bi)-(Si,Ge)-O oxide glasses
The effect of the reduction process in H2 at 380 °C on the microstructure and elemental composition of a glass Bi0.4Pb0.2Si0.4Ox has been investigated. It has been shown that after reduction a clearly separated top layer with a thickness of approx. 50 µm was formed on the surface of the sample. This layer is depleted of oxygen and has higher electrical conductivity than the interior of the glass. It has also been found that some granules of metallic bismuth with a diameter of tens to hundreds of nanometers were formed on the surface of the glass. Furthermore, depletion of lead was observed in these samples in relation to the initial stoichiometry of the glass prior to trial reduction.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE W OKRESIE WAKACYJNYM BIBLIOTEKA BĘDZIE FUNKCJONOWAŁA W ZMIENIONYCH GODZINACH::
od 15 do 31 lipca:
Wypożyczalnia i Czytelnia Główna:
9.00 - 15.00
(poniedziałek-piątek)
Czytelnia Działu Zbiorów Specjalnych:
9.00 - 15.00
(poniedziałek-piątek)
od 1 do 31 sierpnia:
BIBLIOTEKA BĘDZIE NIECZYNNA
UWAGA:
Zwrotu wypożyczonych materiałów można dokonać u dyżurującego bibliotekarza w Wypożyczalni Głównej od 9.00 do 15.00.
Na pozycje, których termin zwrotu przypadnie od 1 do 31 sierpnia, wprowadzona zostanie prolongata (nowy termin zwrotu – 6 września).