Dielectric-spectroscopic and ac conductivity studies on 0.01 and 1.0 molar percentage manganese doped layered $Na_{1.86}Li_{0.10}K_{0.04}Ti_3O_7$ ceramics have been reported. The dependence of loss tangent (tan δ) and relative permittivity ($ε_{r}$) on temperature in the range 350-775 K and on frequency in the range 10 kHz-1 MHz have been undertaken. The losses are the characteristics of dipole mechanism, electrical conduction and space charge polarization. The obtained conductivity plots between log($σ_{ac}T$) versus 1000/T have been divided into four regions namely region I, II, III, and IV. The mechanism of conduction in region I is acknowledged to electronic hopping conduction. The less frequency and more temperature dependent region II is ascribed as a mixed mechanism "associated interlayer ionic conduction, electron hopping, and alkali ion hopping conduction". The unassociated interlayer ionic conduction along with alkali ion hopping conduction mechanisms are contributing to the transport process in the mid temperature region III. The mechanism of conduction in the highest temperature region IV may be recognized as the modified interlayer ionic conduction. The conductivity versus frequency curves lead to conclude that the electronic hopping conduction diminishes with the rise of temperature.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00