This paper is intended to highlight the effect of copper addition on the pitting corrosion resistance of aluminium-base powder metallurgy parts. Results obtained on these mechanically alloyed (MA) specimens are compared with parts of MA-Al without added copper, as well as with commercial aluminium alloys. Immersion tests from 2 to 96 hours in 3.5% NaCl solutions, and potentiostatic techniques, were used to study the pitting corrosion. It was concluded that copper addition, in a similar way that in commercial aluminium alloys, produces a negative effect on the pitting corrosion resistance, because of the formation of Al₂Cu. These precipitates produce galvanic cells that favour the specimen pit. Therefore, increasing the copper content of MA-Al, although improving their ductility, worsens the pitting corrosion resistance of these alloys.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00