Magnetic and magnetotransport properties of La0.5Sr0.5Co0.8Me0.2O3 (Me=Cr, Fe) cobaltites

Magnetic and magnetotransport properties of La0.5Sr0.5Co0.8Me0.2O3 (Me = Cr, Fe) stoichiometric cobaltites has been investigated in magnetic fields up to 14 T. It is shown that doping with Fe ions changes spontaneous magnetization only slightly herewith the Curie point significantly decreases. The chromium doping leads to dramatic decrease of magnetization and the Curie point and a strong increase in magnetoresistance at low temperature. The obtained results indicate that the magnetic interactions between Co and Fe are positive whereas those between Co and Cr ions are negative. Enhancement of magnetoresistance is attributed to the magnetic field induced transition from antiferromagnetic order to ferromagnetic one.

Właściwości magnetyczne i magnetotransportowe stoichiometrycznych kobaltytów zbadano w polach magnetycznych do 14T. Ustalono, że domieszkowanie przez jony Fe zmienia namagnesowanie spontaniczne bardzo słabo w tym czasie jak punkt Curie obniża się znacząco. Domieszkowanie przez atomy chromu powoduje dramatyczne zmniejszenie namagnesowania i obniżenie punktu Curie i mocny wzrost magneto rezystancji w niskich temperaturach. Otrzymane rezultaty wskazują oddziaływanie magnetyczne pomiędzy Co i Fe jest pozytywne w tym czasie jak pomiędzy Co a Cr jest negatywne. Wzmocnienie magnetorezystancji przypisano do pola magnetycznego indukowanego przejściem z antyferromagnetycznego układu do ferromagnetycznego.