Electronic-and-optical properties of Rb2ZnCl4 crystals

Electronic-and-optical properties of Rb2ZnCl4 crystal have been studied using the theoretical and experimental methods. First principles calculations of the electronic structure and optical properties using the density functional theory have been performed on the relaxed and uniaxially compressed (1 GPa) Rb2ZnCl4 crystal. The refractive indices of Rb2ZnCl4 have been measured in the spectral range of wavelength 300 nm to 750 nm for three principal uniaxial compression stresses (0.02 GPa) at room temperature. Ab initio calculations and analysis have revealed that the observed uniaxial pressure changes of the refractive indices of Rb2ZnCl4 are caused mainly by the corresponding changes of the crystal unit cell dimensions. The unit cell electronic polarizability of the crystal remains approximately unchanged.

Zbadano właściwości elektronowo-optyczne kryształów Rb2ZnCl4 metodami teoretyczną i doświadczalną. Wykonano obliczenia z pierwszych zasad (ab initio) struktury elektronowej i właściwości optycznych na bazie teorii funkcjonału gęstości zrelaksowanych i jednoosiowo ściśniętych (1 GPa) kryształów. Zostały pomierzone współczynniki załamania Rb2ZnCl4 w przedziale długości fal światła 300 nm do 750 nm dla trzech głównych krystalograficznych kierunków ściskania (0.02 GPa) przy temperaturze pokojowej. Obliczenia ab initio i analiza danych ujawniły, że obserwowane baryczne zmiany współczynników załamania Rb2ZnCl4 są spowodowane głównie odpowiednimi zmianami rozmiarów komórki elementarnej kryształu. Przy tym, polaryzowalność elektronowa komórki kryształu pozostaję się prawie niezmienną.