Welding supports of pins in mobile platforms

The demand for dissimilar joints of hard-welded steels used in civil engineering and transport is increasing. An example of this can be welding of pins of high-strength steel S690 QL (1.8928) with the arms of a movable platform made of DOCOL 1200M steel from the AHSS group. This joint is difficult to make properly, due to significant differences in the thickness of welded elements and different chemical composition of both steels. The diameter of pin is 40 mm. The thickness of the metal sheet used for the mobile platform arm is 2 mm. Joints of varying thickness and chemical composition may have cracks in the heat affected zone and in the weld. The purpose of the article is to determine the welding parameters and the selection of filler materials that will allow to obtain the correct joint without welding defects.

Wzrasta zapotrzebowanie na wykonywanie mieszanych złączy z trudnospawalnych stali stosowanych w inżynierii lądowej i w transporcie. Przykładem tego może być spawanie sworzni z konstrukcyjnej stali o podwyższonej wytrzymałości S690 QL (1.8928) z ramionami podestu ruchomego wykonanego ze stali DOCOL 1200M z grupy AHSS. Złącze to jest trudne do prawidłowego wykonania, ze względu na znaczne różnice grubości spawanych elementów i odmienny skład chemiczny oraz mechanizmy umocnienia obu stali. Średnica sworznia wynosi 40 mm. Grubość blachy stosowanej na ramię podestu jest znacznie mniejsza - 2 mm. W złączach o różnej grubości i odmiennym składzie chemicznym mogą występować pęknięcia w strefie wpływu ciepła i w spoinie. Celem artykułu jest ustalenie parametrów spawania i dobór materiałów dodatkowych, które pozwolą na uzyskanie prawidłowego złącza bez wad spawalniczych.