Laser surface alloying of ductile cast iron with Ti + 5% W mixture

The article presents results of the research on laser alloying of the ductile cast iron EN-GJS 350-22 substrate with the mixture of titanium powder with addition of 5 wt.% of tungsten. The aim of the process was to obtain surface layer with the in-situ composite structure. Laser alloying process was carried out using high power diode laser (HPDDL) with rectangular laser beam focus and uniform power density distribution in one axis of the beam focus (top-hat profile). The tests included determination of the influence of process parameters on the dimensions of the alloyed beads, metallographic macroscopic and microscopic observations, microhardness measurements of the laser alloyed layers and EDS chemical composition tests.

Artykuł przedstawia wyniki badań nad stopowaniem laserowym żeliwa sferoidalnego EN-GJS 350-22 mieszaniną proszku tytanu z dodatkiem 5 %wag. wolframu. Celem procesu było uzyskanie warstwy wierzchniej o strukturze kompozytowej metodą in-situ. Proces stopowania przeprowadzony został z wykorzystaniem lasera diodowego dużej mocy HPDDL o ognisku prostokątnym i równomiernym rozkładzie gęstości mocy w jednej osi ogniska (top-hat profile). Badania obejmowały określenie wpływu parametrów procesu na wymiary ściegów stopowanych, obserwacje makroskopowe i mikroskopowe, pomiary mikrotwardości uzyskanych warstw wierzchnich oraz badania składu chemicznego EDS.